Great Chemical Resistance Perfluoroelastomer Compound
FUDI imapereka mitundu itatu yaperfluoroelastomer ffkmgulu & ffkm polima.
A. Ili ndi kutentha kwakukulu kogwira ntchito komanso kukana kwambiri ndi media media.
Mawonekedwe
● Kukana kwambiri kutentha kwambiri mpaka 300-320 ℃
● Kukana kwapadera kwa mankhwala aukali;
● Kukaniza kwambiri nthunzi;
● Kupanikizika kwapadera kumayikidwa ngakhale kutentha kwambiri;
● Processability ndi muyezo fluoroelastomer luso pa convential mphira zida.
● Mtengo ndi wokwera mtengo kwambiri.
Kugwiritsa ntchito
O-mphete, zisindikizo, diaphragms ndi mbali zina zomwe zimagwiritsidwa ntchito m'mafakitale opangira.
Mtengo wa MOQ
300 gm
Deta zowunikira
Kukana kutentha | |
Kutentha kukalamba 70 h @ 280 ℃ | |
100% Modulus Mpa | 9.5 |
Tensile mphamvu Mpa | 19.5 |
Kuwonjezeka pa nthawi yopuma% | 215 |
Hardness Shore A | 72 |
Kutentha kukalamba 70 h @ 300 ℃ | |
100% Modulus Mpa | 7.5 |
Tensile mphamvu Mpa | 17 |
Kuwonjezeka pa nthawi yopuma% | 260 |
Hardness Shore A | 72 |
Kutentha kukalamba 70 h @ 316 ℃ | |
100% Modulus Mpa | 6.5 |
Tensile mphamvu Mpa | 14 |
Kuwonjezeka pa nthawi yopuma% | 320 |
Hardness Shore A | 72 |
B. Imakhala ndi kutentha kochepa kogwira ntchito komanso kukana kwambiri kwa media media.
Mawonekedwe
● Kukana kwambiri kutentha kwambiri mpaka 250 ~ 260 ℃
● Kukana kwapadera kwa mankhwala aukali;
● Kukaniza kwambiri nthunzi;
● Kupanikizika kwapadera kumayikidwa ngakhale kutentha kwambiri;
● Mtengo ndi wotsika mtengo kuposa giredi A.
Kugwiritsa ntchito
O-mphete, zisindikizo, diaphragms ndi mbali zina zomwe zimagwiritsidwa ntchito m'malo ovuta.
Mtengo wa MOQ
300 gm
Deta zowunikira
Hardness Shore A | 74 |
Mphamvu yokoka / | 1.99 |
Tensile mphamvu Mpa | 24.5 |
100% Modulus Mpa | 7.5 |
Elongation % | 200 |
Kuphatikizika kwakhazikitsidwa 72 h @ 200 ℃ | 18.1 |
Kuphatikizika kwakhazikitsidwa 72 h @ 230 ℃ | 26.7 |
Kukana kwa Chemical (Kwa Ketone, Ester, Ether)
Chemical | Temp | Kusintha pambuyo pa 168hr (%) | Kusintha pambuyo pa 500hr (%) |
Acetone | 40 ℃ | 2.5 | 3.3 |
Methyl ethyl ketone | 2.2 | 3.2 | |
Isophoroni | 0.1 | 0.5 | |
Ethyl acetate | 3.1 | 3.8 | |
Dioxane | 1.2 | 2.0 | |
Methyl isobuthyl ketone | 1.2 | 2.0 | |
Acetylacetone | 0.8 | 1.3 | |
Buthyl acetate | 1.5 | 2.5 | |
Diethyl ether | 25 ℃ | 2.6 | 4.3 |
C. Ili ndi kutentha kochepa kogwira ntchito komanso kukana bwino kwa media media.
Mawonekedwe
● Kukana kwambiri kutentha kwambiri mpaka 240 ℃
● Kukana kwapadera kwa mankhwala aukali;
● Kukaniza kwambiri nthunzi;
● Kupanikizika kwapadera kumayikidwa ngakhale kutentha kwambiri;
● Processability ndi muyezo fluoroelastomer luso pa ochiritsira mphira equipments.
● Mtengo ndi wotsika mtengo.
Deta zowunikira
Kukalamba kwa mpweya wotentha | 300 ℃ × 24Hrs | GB/T 3512-2014 | |||
Kulimba kwamakokedwe | % | -18.1 | |||
Elongation | % | 17.1 | |||
Kusintha kwamphamvu | 0.2 | ||||
Compress set | 23 × 70Hrs | GB/T 7759.1-2015 | |||
Compress set | % | 11.2 | |||
Compress set | 204 ℃ × 70Hrs | GB/T 7759.1-2015 | |||
Compress set | % | 22.7 | |||
Compress set | 250 ℃ × 70Hrs | GB/T 7759.1-2015 | |||
Compress set | % | 33.2 | (Pali ming'alu) | ||
Fule RP-3 | 150 ℃ × 24Hrs | GB/T 1690-2010 | |||
Kulimba kwamakokedwe | % | -14.3 | |||
Elongation | % | 5.8 | |||
Kusintha kwamphamvu | -2 | ||||
Kusintha kwa mawu | % | 4.6 | |||
Kutentha kochepa | GB/T 15256-2014 | ||||
Kutentha kochepa | ℃ | -30 |